Cement mortars richer than 1 : 3 are not used in masonry because(i) There is no gain in strength of masonry(ii) There is high shrinkage(iii) They are prone to segregation

(i), (ii) and (iii) are correct

Cement mortars richer than 1 : 3 are not used in masonry because(i) T

1.	Cement mortars richer than 1 : 3 are not used in masonry because(i) There is no gain in strength of masonry(ii) There is high shrinkage(iii) They are prone to segregation
A.	Only (ii) is correct
B.	(i) and (ii) are correct
C.	(ii) and (iii) are correct
D.	(i), (ii) and (iii) are correct
Answer» C. (ii) and (iii) are correct

Discussion

No Comment Found

Related MCQs

Assertion A : For identical strength, a composite cement-lime mortar is preferred over cement mortar.Reason R : Composite cement-lime mortar has higher drying shrinkage than cement mortar.Select your answer based on the codes given below. Codes:
Maximum slenderness ratio of load bearing walls for a dwelling having more than 2 storeys(i) Shall not exceed 12 if lime mortar is used(ii) Shall not exceed 18 if cement lime mortar 1 : 2 : 9 is used(iii) Shall not exceed 24 if cement mortar 1 : 6 is used
Direct load carrying capacity of a brick masonry wall standing freely as against when it supports RC slab will be
For masonry built in 1 : 1 : 6 cement-lime-sand mix mortar or equivalent, the horizontal shear stress permissible on the area of a mortar bed joint is
Assertion A : Lime based mortars give higher ratio of brickwork strength to mortar strength as compared to non-lime mortar.Reason R : Lime based mortars have lower bond strength as compared to non-lime mortars.Select your answer according to the codes given below:
Consider the following statements:1. Masonry in rich cement mortar though having good strength with high shrinkage is much liable for surface cracks.2. Lime mortar possesses poor workability and poor water retentivity and also suffers high shrinkage.3. Masonry in lime mortar has better resistance against rain penetration and is less liable to crack when compared to masonry in cement mortar.Which of these statements are correct?
The bending stress in a wall or column subjected to effective vertical load need not be considered, if the eccentricity ratio is
A 200 mm thick brick masonry wall made of modular bricks carries an axial load of 30 kN/m from wall above and an eccentric load of 20 kN/m from RCC floor acting at a distance of 47.5 mm from the centre line of the wall. The resultant eccentricity ratio is
If the eccentricity ratio is more than 1/24, then increase in the permissible stress in the design of wall subjected to eccentric loading as per code is
Rich cement mortars are more liable to cracking as compared to lean mortars because rich mortars have

Cement mortars richer than 1 : 3 are not used in masonry because(i) There is no gain in strength of masonry(ii) There is high shrinkage(iii) They are prone to segregation