| 1. |
Assertion (A): Chills are used to reduce shrinkage porosity.Reason (R): the function of chill is to increase the rate of solidification in a critical region. |
| A. | Both A and R is correct, and R is a correct explanation for A |
| B. | Both A and R is correct, and R is an incorrect explanation for A |
| C. | A is wrong but R is correct |
| D. | A is correct but R is wrong |
| Answer» B. Both A and R is correct, and R is an incorrect explanation for A | |
| 2. |
Which one of the statements is not correct in metal casting? |
| A. | Rapid cooling produces a solidified skin or shell |
| B. | Those grain that have favourable orientation will grow preferentially |
| C. | Cast iron has wide mushy zones |
| D. | Lack of uniformity in grains size and distribution will cause anisotropic properties |
| Answer» D. Lack of uniformity in grains size and distribution will cause anisotropic properties | |
| 3. |
The following characteristic of molten metal influence the fluidity.i) Mushy zoneii) Viscosityiii) Surface tensioniv) InclusionWhich one of the following is correct? |
| A. | i and ii |
| B. | i only |
| C. | i, ii and iii |
| D. | i, ii, iii and iv |
| Answer» E. | |
| 4. |
Dissolved gases may be removed from molten metal by? |
| A. | Flushing or purging with inert gas |
| B. | Melting and pouring the metal in vacuum |
| C. | Flushing or purging with inert gas or Melting and pouring the metal in vacuum |
| D. | Melting and pouring the metal in nitrogen atmosphere |
| Answer» D. Melting and pouring the metal in nitrogen atmosphere | |
| 5. |
Which one of the following expands during solidification? |
| A. | Mild steel |
| B. | Grey cast iron |
| C. | Aluminium |
| D. | Copper |
| Answer» C. Aluminium | |
| 6. |
According to Chvorinov’s rule the solidification time is a function of volume and surface area and is given by the relationship between volume, area and some exponential power ‘n’. What is the value of n? |
| A. | 1 |
| B. | 2 |
| C. | 3 |
| D. | 4 |
| Answer» C. 3 | |
| 7. |
If we decrease the freezing range, then the fluidity of metal will? |
| A. | Increase |
| B. | Decrease |
| C. | Will not change |
| D. | Initially increase and then decrease |
| Answer» B. Decrease | |
| 8. |
WHICH_ONE_OF_THE_STATEMENT_IS_CORRECT_IN_METAL_CASTING??$ |
| A. | Rapid cooling produces a solidified skin or shell |
| B. | Those grain that have favorable orientation will grow preferentially |
| C. | Cast iron has wide mushy zones |
| D. | Lack of uniformity in grains size and distribution will cause anisotropic properties |
| Answer» D. Lack of uniformity in grains size and distribution will cause anisotropic properties | |
| 9. |
Assertion_(A):_Chills_are_used_to_reduce_shrinkage_porosity.$ |
| A. | : the function of chill is to increase the rate of solidification in a critical region. |
| B. | Both A and R is correct and R is a correct explanation for A |
| C. | Both A and R is correct and R is an incorrect explanation for A |
| D. | A is wrong but R is correct |
| Answer» B. Both A and R is correct and R is a correct explanation for A | |
| 10. |
What is the function of cores used in casting? |
| A. | To remove dissolved gases |
| B. | To avoid defects |
| C. | To form hollow region |
| D. | To reduce shrinkage porosity |
| Answer» D. To reduce shrinkage porosity | |
| 11. |
The following characteristic of molten metal influence the fluidity |
| A. | Mushy zone |
| B. | Viscosity |
| C. | Surface tension |
| D. | Inclusion |
| Answer» E. | |
| 12. |
Solidification of casting does not depend upon which factor? |
| A. | Type of metal |
| B. | Thermal properties of metal |
| C. | Geometric relationship between volume and surface area |
| D. | Surface tension. |
| Answer» E. | |
| 13. |
Doubling the time in flat mould will increase the thickness of wall skin by what percentage? |
| A. | 31.6% |
| B. | 41% |
| C. | 73% |
| D. | 22% |
| Answer» C. 73% | |
| 14. |
Dissolved gases may be removed from molten metal by |
| A. | Flushing or purging with inert gas |
| B. | Melting and pouring the metal in vacuum |
| C. | Flushing or purging with inert gas or Melting and pouring the metal in vacuum |
| D. | None of the Mentioned |
| Answer» D. None of the Mentioned | |
| 15. |
Which one of the following expands during contraction? |
| A. | Mild steel |
| B. | Grey cast iron |
| C. | Aluminium |
| D. | Copper |
| Answer» C. Aluminium | |
| 16. |
According to Chvorinov’s rule the solidification time is a function of volume and surface area and is given by the relationship between volume, area and some exponential power ‘n’. Here the value of n is$ |
| A. | 1 |
| B. | 2 |
| C. | 3 |
| D. | 4 |
| Answer» C. 3 | |
| 17. |
If we decrease the freezing range then the fluidity of metal will? |
| A. | Increase |
| B. | Decrease |
| C. | Will not change |
| D. | Will increase then decrease |
| Answer» B. Decrease | |