How does heating for hypereutectoid steels differ from hypoeutectoid s – McqOptions

MCQOPTIONS

1.	How does heating for hypereutectoid steels differ from hypoeutectoid steels?
A.	Heated 30-60<sup>o</sup>C above A1 line
B.	Heated 30-60<sup>o</sup>C below A1 line
C.	Heated 30-60<sup>o</sup>C below A2 line
D.	Heated 30-60<sup>o</sup>C below A3 line
Answer» B. Heated 30-60<sup>o</sup>C below A1 line

Discussion

No Comment Found

Related MCQs

THE_ONE_SPECIMEN_FORM_ABOVE_MENTIONED_SPECIMEN_IS_COLD_WORKED.?$
HEATING_OF_HYPEREUTECTOID_STEELS_RESULTS_IN_FORMATION_OF_COARSE_PEARLITE_WITH_EXCESS___________?$
THE_ANISOTHERMAL_ANNEAL_METHOD,_THE_ENERGY_RELEASE_IS_DETERMINED_AS_A_FUNCTION_OF_TEMPERATURE.?$
How does heating for hypereutectoid steels differ from hypoeutectoid steels?
Free energy of cold-worked metals is _____ than/as that of annealed metals?
What is the result of full annealing of hypoeutectoid steels?
Which of the following relations is true?
Cooling of hypoeutectoid steels in done is furnace by decreasing the temperature to at least ________ below the A1 line.
Vacancies in the metal lattice will be formed in greater numbers than interstitial atoms during _____
For full annealing of hypoeutectoid steels, they are heated in a range above __________