Explore topic-wise MCQs in Casting.

This section includes 17 Mcqs, each offering curated multiple-choice questions to sharpen your Casting knowledge and support exam preparation. Choose a topic below to get started.

1.

Directional solidification always ends at the sprue part and starts from the end of the casting.

A. True
B. False
Answer» B. False
Discussion
2.

In the process of directional solidification, weight always remains constant for all the materials.

A. True
B. False
Answer» C.
Discussion
3.

Which of the following methods is used for the cutting of directionally solidified rods or castings?

A. Thermal cutting
B. Electro-discharge machining
C. Water jet cutting
D. Weld cutting
Answer» C. Water jet cutting
Discussion
4.

To achieve useful strength of the material at temperatures of 1000-1600 ⁰C, what should be the melting point temperature of the material?

A. 1000 ⁰C
B. 1300 ⁰C
C. 1600 ⁰C
D. More than 1600 ⁰C
Answer» E.
Discussion
5.

It is not easy to control the material at the microstructure level in the directional solidification.

A. True
B. False
Answer» C.
Discussion
6.

WHICH_OF_THE_FOLLOWING_METHODS_IS_USED_FOR_THE_CUTTING_OF_DIRECTIONALLY_SOLIDIFIED_RODS_OR_CASTINGS??$

A. Thermal cutting
B. Electro-discharge machining
C. Water jet cutting
D. Weld cutting
Answer» C. Water jet cutting
Discussion
7.

Directional solidification always ends at the sprue part and starts from the end of the casting$

A. True
B. False
Answer» B. False
Discussion
8.

In_the_process_of_directional_solidification,_weight_always_remains_constant_for_all_the_materials.$

A. True
B. False
Answer» C.
Discussion
9.

Progressive solidification is better than the directional solidification and it is independent to the geometry of mould.

A. True
B. False
Answer» C.
Discussion
10.

Which of the following furnaces is used for the directional solidification of cast ingots of eutectic?

A. Pneumatic zone furnace
B. Cupola furnace
C. Hydraulic zone furnace
D. Optical floating zone furnace
Answer» E.
Discussion
11.

Which of the following shows the relationship between the growth rate and inter-phase spacing?

A. λ<sup>2</sup>R = constant
B. λR<sup>2</sup> = constant
C. λ/R = constant
D. λ⁴R = constant
Answer» B. ‚âà√≠¬¨‚Ñ¢R<sup>2</sup> = constant
Discussion
12.

To achieve useful strength of the material at temperatures of 1000-1600 ‚Äö√Ö‚àûC, what should be the melting point temperature of the material?$

A. 1000 ‚Äö√Ö‚àûC
B. 1300 ‚Äö√Ö‚àûC
C. 1600 ‚Äö√Ö‚àûC
D. More than 1600 ‚Äö√Ö‚àûC
Answer» E.
Discussion
13.

Oxidation resistance should be the prime requirement for the high temperature structural applications.

A. True
B. False
Answer» B. False
Discussion
14.

It is not possible to replace super-alloys by the directionally solidified high temperature eutectics.

A. True
B. False
Answer» C.
Discussion
15.

It is not easy to control the material at microstructure level in the directional solidification.

A. True
B. False
Answer» C.
Discussion
16.

Directional solidification allows components to be produced from the melt in a single stage process.

A. True
B. False
Answer» B. False
Discussion
17.

Which of the following materials has superior strength and rigidity at high elevated temperature?

A. Aluminium-based alloys
B. Copper-based alloys
C. Zinc-based alloys
D. Nickel-based alloys
Answer» E.
Discussion