1.	During recrystallization, the boundaries between the new strain-free grains and the original deformed grains are acted on by a force G /V where, in this case, G is due to the difference in dislocation strain energy between the two grains.
A.	False
B.	True
Answer» C.

Discussion

No Comment Found

Related MCQs

If unit area of grain boundary advances a distance 4mm, the number of moles of material that enter in the grain B is 4* (1/ 8(mm<sup>3</sup>/mol)) and the free energy released is given by_______ ( G =10kJ/mol)
On heating to a sufficiently high temperature, what happens to the new grains?
It is possible that the higher mobility of special grain boundaries plays a role in the development of recrystallization textures.
For low mole fractions of solute in the matrix 0.5 (Xo), the boundary solute concentration Xb (in 10<sup>-1</sup><sup>2</sup>) is given by_____ ( G =105kJ/Mol, T =505K)
During recrystallization, the boundaries between the new strain-free grains and the original deformed grains are acted on by a force G /V where, in this case, G is due to the difference in dislocation strain energy between the two grains.
Calculate the chemical potential if the molar volume is given as 5 mm<sup>3</sup>/mol? (Given the value of radius as 4mm and the interfacial energy is 8 kJ/mm<sup>2</sup>?
Calculate the pulling force F, if the chemical potential and the molar volume is given as respectively?
Under which of the following circumstances the grain boundary behaves as a thin soap film?
What will be the torque acting on the boundary if the boundary happens to be at the orientation of a cusp in the free energy?
What is the need for a grain boundary in an annealed material?