This section includes 13 Mcqs, each offering curated multiple-choice questions to sharpen your Advanced Machining knowledge and support exam preparation. Choose a topic below to get started.
| 1. |
DURING_ROUGHING_PROCESS_THROUGH_ELECTRO_DISCHARGE_MACHINING,_WHAT_IS_THE_THICKNESS_OF_LAYER_FORMED??$ |
| A. | <0.075 mm |
| B. | <0.125 mm |
| C. | <0.500 mm |
| D. | <0.750 mm |
| Answer» C. <0.500 mm | |
| 2. |
Which of the following processes can be used for restoration of fatigue properties?$ |
| A. | Low-stress grinding |
| B. | Chemical machining |
| C. | Reheat treatment |
| D. | All of the mentioned |
| Answer» E. | |
| 3. |
During finishing process through Electro discharge machining, what is the value thickness of layer formed?$ |
| A. | <0.075 mm |
| B. | <0.125 mm |
| C. | <0.500 mm |
| D. | <0.750 mm |
| Answer» B. <0.125 mm | |
| 4. |
State whether following statement is true or false regarding the HAZ in EDM. |
| A. | |
| B. | True |
| Answer» C. | |
| 5. |
The altered layers formed during the process of EDM consists of which of the following? |
| A. | Tempered layers |
| B. | Heat affected zones |
| C. | Intergranular precipitates |
| D. | All of the mentioned |
| Answer» E. | |
| 6. |
What happens to the fatigue strength of alloys if altered surfaces are produced in Electro discharge machining? |
| A. | Increases |
| B. | Reduces |
| C. | Enhances |
| D. | Improves |
| Answer» C. Enhances | |
| 7. |
In EDM, choosing electrodes that produce which type of machining reduces the annealing effect? |
| A. | Stable |
| B. | Unstable |
| C. | Uneven |
| D. | All of the mentioned |
| Answer» B. Unstable | |
| 8. |
What are the values of thickness of annealed surface obtained while machining using EDM? |
| A. | 1 to 25 µm |
| B. | 50 to 200 µm |
| C. | 200 to 500 µm |
| D. | 500 to 1000 µm |
| Answer» C. 200 to 500 ¬¨¬®¬¨¬µm | |
| 9. |
The depth of the annealed surface is _____ to the amount of power used in machining operation. |
| A. | Directly proportional |
| B. | Inversely proportional |
| C. | Exponential |
| D. | All of the mentioned |
| Answer» B. Inversely proportional | |
| 10. |
In Electro discharge machining, some annealing of the work piece can be expected _____ the machined surface. |
| A. | On |
| B. | Just below |
| C. | Above |
| D. | At bottom |
| Answer» C. Above | |
| 11. |
What are the values of thickness of recast layers in Electro discharge machining? |
| A. | 0.001 to 0.025 µm |
| B. | 0.01 to 0.25 µm |
| C. | 1 to 25 µm |
| D. | 10 to 250 µm |
| Answer» D. 10 to 250 ¬¨¬®¬¨¬µm | |
| 12. |
What is the value of thickness of recast layer obtained when power of 5 µJ is given?$ |
| A. | 1 µm |
| B. | 3 µm |
| C. | 5 µm |
| D. | 7 µm |
| Answer» B. 3 ¬¨¬®¬¨¬µm | |
| 13. |
What are the values of temperatures obtained in Electro discharge machining? |
| A. | 1000 to 2000 <sup>o</sup>C |
| B. | 2000 to 4000 <sup>o</sup>C |
| C. | 4000 to 8000 <sup>o</sup>C |
| D. | 8000 to 12000 <sup>o</sup>C |
| Answer» E. | |